Hbond-802 tile grout:
Hbond-802 Tile adhesive is a three component synthetic mortar on epoxy resin based . Component A(epoxy resin),component, B(hardener) and component C(aggregates C)powder it is soluble with high adhesion, Component A and component B is liquid.
Technical data:
Physical property | Appearance A:B:C, paste | Test conditions | Results |
Mechanical property | Flexural tensile strength | 25℃28days | ≥ 8kg/cm2 |
compression strength | 25℃28days | ≥ 35 kg/cm2 | |
Adhesive strength | 25℃28days | ≥12kg/cm2 | |
Coefficient of thermal expansion | temperature range (from-15℃to +20℃) 25 times | Keep stable | |
Heat -resistant | 100℃ hot water , 5 hours | keep stable | |
Chemical resistance | Ca(OH)2 ,168 hours | keep stable | |
Sag Flow | On vertical surfaces it is non-sag up to 9-10 mm thickness | ||
Features:
This product has excellent adhesion ,flexibility and impermeability, which is waterproof ,
crack-resistant and resistant to freezing and thawing in hot and cold shock, it can improve the
surface of aging and long term durability. it can bond brick,ceramic,marble,mosaic and
so on. This product does not contain formaldehyde, benzene, toluene + xylene and total volatile
organic compounds. Environmental protect.
Applicable environmental:
Indoor-- outdoor--wall--ground --water pool --bathroom --kitchen --cold region
Healthy and safety information:
Wear protective clothing ,goggles ,gloves and /or barrier cream.in case of contact with skin ,wash with plenty of water, in case of contact with eyes. flush with water immediately and consult a physician.
Substrate preparation:
Clean substrate ,remove laitance, curing compounds. and other coating ,oil. grease. rust. waxes and other bond-inhibiting substance. all surface must be clean, sound .clean by mechanical. abrasion methods .such as sandblasting. concrete maybe dry. Moist or in a saturated surface dry condition
Mixing:
Stir components before proportioning. measure out 3 parts components and 1 part component B into pail immediately prior to use. Use with small drum mixer or slow speed (4000-600rpm ) electric drill equipped with a mixing paddle for min of 3-4 minutes. Until blend is uniform .don't dilute mix Add aggregates component C to blended epoxy and continue to mix until uniformly blended .then use
Shelf life:
12 months in original unopened packaging. Store dry at 5°-30°C. Condition product to 10-30°C before using.
Packaging/yield:
Component A 3 kg
Component B 1 kg
Component C 16 kg /bag
Packaging :
Pre-dosed package for ready use 20kg (comp A+B+C)
Mixing Ratio
Ratio A:B:C by weight 3:1:16